Basic Info
Model NO.: alloy 3003 yonghong-5
Alloy: Alloy
Tensile Strength: 260 MPa
Yield Strength: 215 MPa
Elongation: 10%
Hbs Hardness: Hbs10/500
Fatigue Resistance: 125 MPa
Type: Aluminum Strips
Shape: Flat
Product Description
1100/1050/1060/1200 Aluminum features:Pure Industry Aluminum material,it cannot to be heat treatment, high electro conductibility, and heat conductibility,good formability,bending and extending.
Application: Chemical and food storage, electric conductor, soft pipe for brewing industry, heat exchanger, decoration etc
Aluminum strips alloy grades: 1050/1060/1070/1100/1200/1235/3003/3105/3A21
Temper: O H12 H14 H16 H18 H22 H24 H26 H32 H34 H36
Thickness:0.2-4mm
Width:10-2300mm
I.D. Diameter:500 mm.
Aluminum Alloy | Tensile strength | Brinell hardness | fatigue strength | ||
σb/Mpa | σ0.2/Mpa | δ/% | HBS10/500 | /Mpa | |
1060-O | 70 | 30 | 43 | 19 | 20 |
1060-H12 | 85 | 75 | 16 | 23 | 30 |
1060-H14 | 100 | 90 | 12 | 26 | 35 |
1060-H16 | 115 | 105 | 8 | 30 | 45 |
1060-H18 | 130 | 125 | 6 | 35 | 45 |
1100-O | 90 | 25 | 25 | 23 | 35 |
1100-H12 | 110 | 105 | 12 | 28 | 40 |
1100-H14 | 125 | 115 | 9 | 32 | 50 |
1100-H16 | 145 | 140 | 6 | 38 | 60 |
1100-H18 | 165 | 150 | 5 | 44 | 60 |
1050-O | 76 | 28 | 39 | ||
1050-H14 | 110 | 103 | 10 | ||
1050-H16 | 131 | 124 | 8 | ||
1050-H18 | 159 | 145 | 7 | ||
Aluminum Alloy | Tensile strength | Brinell hardness | fatigue strength | ||
σb/Mpa | σ0.2/Mpa | δ/% | HBS10/500 | /Mpa | |
2011-T3 | 380 | 295 | 13 | 95 | 125 |
2011-T78 | 405 | 310 | 12 | 100 | 125 |
2014-O | 185 | 95 | 16 | 45 | 90 |
2014-T4,T415 | 425 | 290 | 18 | 105 | 145 |
2014-T6,T651 | 485 | 415 | 11 | 135 | 125 |
2014-O | 170 | 70 | 21 | ||
2014-T3 | 435 | 275 | 20 | ||
2014-T4,T451 | 421 | 255 | 22 | ||
2014-T6,T651 | 470 | 415 | 10 | ||
2017-O | 180 | 70 | 45 | 90 | |
2017-T4,T451 | 425 | 275 | 105 | 125 | |
2018-T61 | 420 | 315 | 105 | 125 | |
2024-O | 185 | 75 | 20 | 47 | 90 |
2024-T3 | 485 | 345 | 18 | 120 | 140 |
2024-T4,T351 | 470 | 325 | 20 | 120 | 140 |
2024-T361 | 495 | 395 | 13 | 130 | 125 |
2024-O | 180 | 75 | 20 | ||
2024-T3 | 450 | 310 | 18 | ||
2024-T4,T351 | 440 | 290 | 19 | ||
2024-T361 | 460 | 365 | 11 | ||
2024-T81,T851 | 450 | 325 | 6 | ||
2024-T861 | 480 | 395 | 6 | ||
2025-T6 | 400 | 255 | 110 | 125 | |
2036-T4 | 300 | 195 | 24 | 125 | |
2117-T4 | 295 | 165 | 70 | 95 | |
2218-T72 | 330 | 255 | 95 | ||
2219-O | 170 | 75 | 18 | ||
2219-T42 | 360 | 185 | 20 | ||
2219-T31,T351 | 360 | 250 | 17 | ||
2219-T37 | 395 | 315 | 11 | ||
2219-T62 | 415 | 290 | 10 | 105 | |
2219-T81,T851 | 455 | 350 | 10 | 105 | |
2219-T87 | 475 | 395 | 10 | 105 | |
2618-T61 | 625 | 530 | 115 | 18 | |
Aluminum Alloy | Tensile strength | Brinell hardness | fatigue strength | ||
σb/Mpa | σ0.2/Mpa | δ/% | HBS10/500 | /Mpa | |
3003-O | 110 | 40 | 30 | 28 | 50 |
3003-H12 | 130 | 125 | 10 | 35 | 55 |
3003-H14 | 150 | 145 | 8 | 40 | 60 |
3003-H16 | 175 | 170 | 5 | 47 | 70 |
3003-H18 | 200 | 185 | 4 | 55 | 70 |
3004-O | 180 | 70 | 20 | 45 | 95 |
3004-H32 | 215 | 170 | 10 | 52 | 105 |
3004-H34 | 240 | 200 | 9 | 63 | 105 |
3004-H36 | 260 | 230 | 5 | 70 | 110 |
3004-H38 | 285 | 250 | 5 | 77 | 110 |
3105-O | 115 | 55 | 24 | ||
3105-H12 | 150 | 130 | 7 | ||
3105-H14 | 170 | 150 | 5 | ||
3105-H16 | 195 | 170 | 4 | ||
3105-H18 | 215 | 195 | 3 | ||
3105-H25 | 180 | 160 | 8 | ||
4032-T6 | 380 | 315 | 120 | 110 | |
Aluminum Alloy | Tensile strength | Brinell hardness | fatigue strength | ||
σb/Mpa | σ0.2/Mpa | δ/% | HBS10/500 | /Mpa | |
5005-O | 125 | 40 | 25 | 28 | |
5005-H12 | 140 | 130 | 10 | ||
5005-H14 | 160 | 150 | 6 | ||
5005-H16 | 180 | 170 | 5 | ||
5005-H18 | 200 | 195 | 4 | ||
5005-H32 | 140 | 115 | 11 | 36 | |
5005-H34 | 160 | 140 | 8 | 41 | |
5005-H36 | 180 | 165 | 6 | 46 | |
5005-H38 | 200 | 185 | 5 | 51 | |
5050-O | 145 | 55 | 24 | 36 | 85 |
5050-H32 | 170 | 145 | 9 | 46 | 90 |
5050-H34 | 190 | 165 | 8 | 53 | 90 |
5050-H36 | 205 | 180 | 7 | 58 | 95 |
5050-H38 | 220 | 200 | 6 | 63 | 95 |
5052-O | 195 | 90 | 25 | 47 | 110 |
5052-H32 | 230 | 195 | 12 | 60 | 115 |
5052-H34 | 260 | 215 | 10 | 68 | 125 |
5052-H36 | 275 | 240 | 8 | 73 | 130 |
5052-H38 | 290 | 255 | 7 | 77 | 140 |
5456/5056-O | 290 | 150 | 65 | 140 | |
5056-H118 | 435 | 405 | 105 | 150 | |
5056-H38 | 415 | 345 | 100 | 150 | |
5082-O | 275 | 135 | 22 | ||
5082-H34 | 330 | 215 | 16 | ||
5082-H38 | 365 | 300 | 8 | ||
5083-O | 290 | 145 | |||
5083-H321,H116 | 315 | 230 | 130 | ||
5086-O | 260 | 115 | 22 | ||
5086-H32,H116 | 290 | 205 | 12 | ||
5086-H34 | 325 | 255 | 10 | ||
5086-H112 | 270 | 130 | 14 | ||
5154-O | 240 | 115 | 27 | 58 | 115 |
5154-H32 | 270 | 205 | 15 | 67 | 125 |
5154-H34 | 290 | 230 | 13 | 73 | 130 |
5154-H36 | 310 | 250 | 12 | 78 | 140 |
5154-H38 | 330 | 270 | 10 | 80 | 145 |
5154-H112 | 240 | 115 | 25 | 63 | 115 |
5182-O | 290 | 145 | 21 | ||
5182-H34 | 330 | 230 | 18 | ||
5182-H38 | 380 | 310 | 9 | ||
5252-H25 | 235 | 170 | 11 | 68 | |
5252-H38,H28 | 285 | 240 | 5 | 75 | |
5254-O | 240 | 115 | 27 | 58 | 115 |
5254-H32 | 270 | 205 | 15 | 67 | 125 |
5254-H34 | 290 | 230 | 13 | 73 | 130 |
5254-H36 | 310 | 250 | 12 | 78 | 140 |
5254-H38 | 330 | 270 | 10 | 80 | 145 |
5254-H112 | 240 | 115 | 25 | 63 | 115 |
5454-O | 250 | 115 | 22 | 62 | |
5454-H32 | 275 | 205 | 10 | 73 | |
5454-H34 | 305 | 230 | 10 | 81 | |
5454-H111 | 260 | 180 | 14 | 70 | |
5454-H112 | 250 | 125 | 18 | 62 | |
5456-O | 310 | 160 | |||
5456-H112 | 310 | 165 | |||
5456-H321,H116 | 350 | 255 | 90 | ||
5457-O | 130 | 50 | 22 | 32 | |
5457-H25 | 180 | 160 | 12 | 48 | |
5457-H38,H28 | 205 | 185 | 6 | 55 | |
5652-O | 195 | 90 | 25 | 47 | 110 |
5652-H32 | 230 | 195 | 12 | 60 | 115 |
5652-H34 | 260 | 215 | 10 | 68 | 125 |
5652-H36 | 275 | 240 | 8 | 73 | 130 |
5652-H38 | 290 | 255 | 7 | 77 | 140 |
5657-H25 | 160 | 140 | 12 | 40 | |
5657-H38,H28 | 195 | 165 | 7 | 50 | |
6061-O | 125 | 55 | 25 | 30 | 60 |
6061-T4,T451 | 240 | 145 | 22 | 65 | 95 |
6061-T651 | 310 | 275 | 12 | 95 | 95 |
Chemical composition | |||||||||
Si | Fe | Cu | Mn | Mg | Zn | Ti | Others | Al | |
single | total | ||||||||
0.5 | 0.5 | 0.1 | 0.3-0.6 | 4.8-5.5 | 0.2 | - | 0.05 | 0.1 | Balance |