aluminum welding wire 5356 for the weldig of aluminum sheet

Home »  Products »  Aluminum Sheet »  aluminum welding wire 5356 for the weldig of aluminum sheet

Aluminum Welding Wire 5356 For The Weldig Of Aluminum Sheet

Quick Details


Material: Aluminum / Aluminum Alloy
Diameter: 1.2mm-5.0mm
Melting Point: International Standard
Weight: 7kg/roll
Application: Ship, locomotive, chemical industry, shipbuilding, aviation
Flux Content: Standerd
Color: Silver
Packing: 0.5kg/ Spool, 2kg/Spool, 7kg/Spool
size: 1.2/1.6/2.0/2.4/3.0/4.0/5.0mm
OEM: Accept
Product name: aluminium wire ER4043/ER5356
Trade term: FOB/CIF/CFR
Payment: T/T,L/C
Sample: free sample
Certificate: CCS
Feature: Excellent Welding Performance

Packaging


Mig: 7kg/roll;
Tig: 10kg/piece,20kg/canton
1ton/pallet

Delivery


Receipt of L/C or T/ 5-10days of shipment

ER4043 / ER4047 aluminium silicon welding wire


A silicon alloyed aluminium weliding wire the welding of heat-treatable bass alloys and more specifically,the 6*** series alloys,it can also be used for joining wrought to cast materials and is less sensitive to weld cracking silicon in the wire increase puddle fluidity,resulting in excellent operator appeal. Mainly used in ships, locomotives, chemicals, food, sports equipment, mold, furniture, containers, containers, etc.

ER5356 aluminium magnesium welding wire


The welding wire is specially designed for the welding of 5*** series alloy and the chemical composition of the filler alloy and the parent material, which has good corrosion resistance and color property after the anodic treatment. Mainly used for bicycles, scooters and other sports equipment aluminum, carriages, chemical vessels, ordnance production, shipbuilding, aviation etc.
ER1070 Pure aluminum wire
For MIG and TIG welding of pure aluminum welding wire. This kind of welding wire in the anode after treatment has a very good color ratio. Mainly used in ship sports equipment, power (argon arc welding)

GBSAL4043SAL5356SAL 1070SAL4047
AWSER4043ER5356ER1070ER4047
 

Chemical Component

Si4.5-6.0≤0.25≤0.2011.0-13.0
Fe≤0.80≤0.40≤0.25≤0.80
Cu≤0.30≤0.10≤0.04≤0.30
Mn≤0.05

Mg≤0.05

0.05-0.20

Mg4.5-5.5

≤0.03≤0.15
Zn≤0.10≤0.10

Cr 0.05-0.20

≤0.04≤0.20
Ti≤0.200.06- 0.20≤0.03Mg ≤0.10
Alrestrest≥99.70rest
TIGDia

mm

1.6-2.4

2.4-4.0

4.0-5.0

1.6-2.4

2.4-4.0

4.0-5.0

2.0-2.4

2.4-4.0

4.0-5.0

1.6-2.4

2.4-4.0

4.0-5.0

Current

A

150-250

200-320

220-400

150-250

200-320

220-400

150-250

200-300

220-400

150-250

200-320

220-400

MIGDia

mm

1.2

1.6

2.0

1.2

1.6

2.0

1.2

1.6

2.0

1.2

1.6

2.0

Current

A

180-300

200-400

240-450

180-300

200-400

240-450

180-300

200-400

240-450

180-300

200-400

240-450

Voltage

V

18-26

20-28

22-32

18-28

20-24

22-34

18-26

20-28

22-32

18-26

20-28

22-32

 

Mechanical Performance of the Deposited Metal

 

(ºC)

Melting

temperature

575-630574-638646-657470-500
conductivity42%IACS29%IACS62%IACS40%IACS
heat conductivity density

2.68g/mm3

 density

2.66g/mm3

210-230W/m.k density

2.68g/mm3

 Mpa

Tensile

Strength

130-160250-300130-160130-160
Mpa

Yield strength

70-120120-16070-8570-85
Elongation10-18%15-25%6-12%6-12%