mill finish 3003 h24 0.7mm thin aluminum coil strips for decoration

Home »  Products »  Aluminum Strip »  mill finish 3003 h24 0.7mm thin aluminum coil strips for decoration

Mill Finish 3003 H24 0.7mm Thin Aluminum Coil Strips For Decoration

Quick Details


Model Number: 3003
Application: Construction, decoration
Thickness: 0.02mm-3.0mm
Width: 20-2400mm
Alloy Or Not: Is Alloy
Grade: 3000 Series
Surface Treatment: Coated
Temper: O - H112
production name: 3003 h24 0.7mm thin aluminum coil strips for decoration
Length: according to your requirements
Surface treated: mill finished
Certification: ISO9001:2008;GJ/B 9001B-2009;ASTMB209
Technical standard: GB/T 3880:2012
Advantage: satisfactory anodizing
Sample: free for charge
MOQ: No MOQ if in stock
Alloy No.: 3003

Product Description


Classification of Aluminum Sheet/Plate

According to alloy composition is divided into


① High purity aluminum plate (the purity above 99.9%)
② Pure aluminum plate
(ingredients made from pure aluminium rolling)
③ Alloy aluminum plate
(composed of aluminum alloy usually with AL and CU, AL and MN, AL and SI, AL and MG etc)
④ Composite aluminum plate or brazing plate
(a variety of material compound for special purposes )

According to thickness is divided into


 Thin aluminum plate: 0.15-2.00mm;

② Regular aluminum plate: 2.0-6.0mm;
③ Moderately thick aluminum plate: 6.0-25.0mm;
④ Heavy aluminum plate: 25-200mm;
⑤ Ultra-thick aluminum plate: more than 200mm;

1000 series Aluminum Sheet Specifications


Type
       Alloy
Temper
Thickness
Width
Application
sheet
1050
O,H12,H14,H16,H18

0.3-0.5mm

0.5-1.0mm

1.0-5.0mm

400-700mm

700-1600mm

>1600mm

Conducors,hoses,,marine accessories.
1060
Chemical and marine equipment
1070
Capacitor ventliation system compents
1100
Reflective devices,pipe,storage,Etc.

1100 Aluminum Sheet Low strength aluminum alloy has excellent corrosion resistance and satisfactory anodizing and conversion coating finishing characteristics. It is unmatched by any other commercial aluminum alloy in workability. Readily to welding, brazing, and soldering. Machinability is poor and tends to be "gummy". Non-heat treatable. 

Temper Description


F
As fabricated (no mechanical property limits specified)
O
Annealed - products achieving the required annealed properties after hot forming processes may be designated as O temper.
H112
Slightly strain-hardened from working at an elevated temperature from a limited amount of cold work (mechanical property limits specified).
T4
Solution heat-treated and naturally aged.
T5
Cooled from an elavated temperature shaping process and then artificially aged.
T6
Solution heat-treated and then artificially aged.
T651
Solution heat-treated, stress-relieved by controlled stretching (permanent set 0.5% to 3% for sheet, 1.5% to 3% for plate, 1% to 3% for rolled or cold finished rod and bar, 1% to 5% for hand or ring forging and rolled ring) and then artificially aged. The products receive no further straightening after stretching.