Zhejiang Shuanglin Jiate Metal Technology Co., Ltd

china mill finish aluminium 3103 roofing coil

Home »  Products »  Aluminum Coil »  china mill finish aluminium 3103 roofing coil

China Mill Finish Aluminium 3103 Roofing Coil

Quick Details


Application: Construction, decoration
Thickness: 0.02mm-3.0mm
Width: 20-2400mm
Alloy Or Not: Is Alloy
Grade: 3000 Series
Surface Treatment: Coated
Temper: O - H112
production name: china mill finish aluminium 3103 roofing coil
Length: according to your requirements
Surface treated: mill finished
Certification: ISO9001:2008;GJ/B 9001B-2009;ASTMB209
Technical standard: GB/T 3880:2012
Advantage: satisfactory anodizing
Sample: free for charge
MOQ: No MOQ if in stock
Alloy No: 3103

 

Classification of Aluminum Sheet/Plate


According to alloy composition is divided into:
① High purity aluminum plate (the purity above 99.9%)

② Pure aluminum plate
(ingredients made from pure aluminium rolling)
③ Alloy aluminum plate
(composed of aluminum alloy usually with AL and CU, AL and MN, AL and SI, AL and MG etc)
④ Composite aluminum plate or brazing plate
(a variety of material compound for special purposes )

 

Feartures Of 3000 series


3000 series aluminum sheet is approx 20% stronger than the 1000 series, has great workability and may be deep drawn, spun, welded or brazed. The 3000series aluminum sheet is widely used for general purposes. The Alloy are including the AA3003, AA3004, AA3005, AA3102, AA3105, Temper O, H14, H18, H24, H26, H111, H112, F, From thickness 0.2mm-350mm, width 500mm-2300mm, length 500mm-110000mm. With Plain, five bar, stucco, diamond, or mirror surface process, Or coated with PE, PVDF, BRUSH etc. There is (CC) cold rolling and (DC) hot rolling Line.

Application Of 3000 series


3003 Aluminum Sheet Approx. 20% higher strength than the 1100 series, but retaining an excellent workability rating. May show some slight discoloration when anodized, but reacts well to mechanical and organic finishings. 3003 is easily welded and brazed, but solder is limited to the torch method. Like 1100, tends to be "gummy" when machined. Non-heat treatable.Typical applications include food and chemical equipment, appliance components, truck and trailer roofing, heat exchangers, and lawn furniture components.

 

Temper Description


F
As fabricated (no mechanical property limits specified)
O
Annealed - products achieving the required annealed properties after hot forming processes may be designated as O temper.
H112
Slightly strain-hardened from working at an elevated temperature from a limited amount of cold work (mechanical property limits specified).
T4
Solution heat-treated and naturally aged.
T5
Cooled from an elavated temperature shaping process and then artificially aged.
T6
Solution heat-treated and then artificially aged.
T651
Solution heat-treated, stress-relieved by controlled stretching (permanent set 0.5% to 3% for sheet, 1.5% to 3% for plate, 1% to 3% for rolled or cold finished rod and bar, 1% to 5% for hand or ring forging and rolled ring) and then artificially aged. The products receive no further straightening after stretching.

 

Why choose us


1.To intergrate globe quality aluminium resources ,to service national industry.

2.More than 10000MT Aluminum ready Stock and cut to pieces is available.

3.Pleased to provide free sample for your confirmation.

4.Promised to offer best quality and price.

5.Quickly feedback within 24 hours